ML 1450 Al99,5Ti

典型成分%

Si <0,25
Fe <0,40
Cu <0,05
Mn <0,05
Mg <0,05
Zn <0,07
Be <0,0003
Ti 0,10-0,20
Others <0,03
Al min. 99,50

分类

EN ISO 18273  :  S Al 1450 ( AI99,5Ti )
Matériel Nr  :  3.0805

基础材料

See table

注意

Welding of pure aluminium requires special precaution due to the narrow melting range in order to prevent hotcracking and porosity. This alloy replaces ML 1050. Consider the technological application reference.

物理性质 (Approx. values)

Electrical conductivity [S*m/mm2]  :  min.35
Heat conductivity at 20°C [W/( m*K )  :  210-230
Linear heat extension coefficient ( 20-100°C ) [1/K]  :  23,5*10-6

纯焊缝金属的物理性能 (Approx. values)

0,2 % yield strength [MPa]  :  20
Tensile strength Rm [MPa]  :  65
Elongation A5 ( L0=5d0 ) [%]  :  35
Test temperature [°C]  :  20

焊接位置

PA, PB, PC, PF

保护气体

I1, I2, I3 (Argon, Helium or Argon/Helium-mixtures)

极性

MIG =+, TIG ~

批准

On request

尺寸

MIG-wires [mm]  :  0,8 ; 1,0 ; 1,2 ; 1,6 ; 2,0 ; 2,4
TIG-rods [mm]  :  1,6 ; 2,0 ; 2,4 ; 3,2 ; 4,0

焊丝包装材料

Spools  :  Packaging units

S 100 / 0,5 kg  :  20 spools = 10 kg (box)
S 200 / 2 kg  :  4 spools = 8 kg (box)
S 300 / 6 kg  :  84 spools = 504 kg (pallet)
B 300 / BS 300 / 7 kg  :  84 spools = 588 kg (pallet)
B 400 / 18 kg  :  28 spools = 504 kg (pallet)
B 400 / 40 kg  :  15 spools = 600 kg (pallet)

Conditionnement baguettes TIG

Carton 5 kg ; carton 10 kg  :  Length 1.000 mm